Grain Size calculation

[syedauc]

Hi All,

I use equivalent radius (diameter) as grain size calculation. My question is when we consider CSL grain boundaries how should I calculate grainsize? To my understanding CSL (like sigma 3, twinning) is considered inside a grain not as boundary. Is there anyway I can exclude the CSL 3 from grain size calculation?

[kilir]

Hi,
usually, one would merge the grains along twin boundaries before saying something about grain size. Have look here: https://mtex-toolbox.github.io/GrainMerge.html
Cheers,
Rüdiger

[syedauc]

Hi Rüdiger , Thanks a lot

…

On Thu, Feb 11, 2021 at 12:02 PM Rüdiger Kilian ***@***.***> wrote: Hi, usually, one would merge the grains along twin boundaries before saying something about grain size. Have look here: https://mtex-toolbox.github.io/GrainMerge.html Cheers, Rüdiger — You are receiving this because you authored the thread. Reply to this email directly, view it on GitHub <#765 (comment)>, or unsubscribe <https://github.com/notifications/unsubscribe-auth/AS2EQ6PAXH23ITG4FW2MZTDS6QESTANCNFSM4XPFZAWQ> .